A335 P11 Liga Azzar Pajp
Oct 20, 2023
A335 P11 Liga Azzar Pajp
SA 335 gr P11 Pajp Seamless Kompożizzjoni Kimika
| C, % | Mn, % | P, % | S, % | Si, % | Cr, % | Lu, % |
| 0.015 Max | 0.30-0.60 | 0.025 Max | 0.025 Max | 0.50 Max | 4.00-6.00 | 0.45-0.65 |
ASTM A335 P11 Proprjetajiet tal-Pajpijiet tal-Azzar
| Qawwa tat-tensjoni, MPa | Qawwa tar-Rendiment, MPa | Titwil, % |
| 415 min | 205 min | 30 min |
Ċart tat-tensjoni tal-P11 Alloy Steel Pajp iwweldjat
| Pajp mingħajr saldatura | ||||||
| P5 | P9 | P11 | P22 | P91 | ||
| Qawwa tat-tensjoni, minima., psi | ||||||
| KSI | 60 | 60 | 60 | 60 | 85 | |
| Mpa | 415 | 415 | 415 | 415 | 585 | |
| Qawwa tar-Rendiment, minimu., psi | ||||||
| KSI | 30 | 30 | 30 | 30 | 60 | |
| Mpa | 205 | 205 | 205 | 205 | 415 | |