X'inhu l-materjal ta 'A335 Pipe
ASTM A335 huwa azzar tal-liga tal-kromju ferritiku mingħajr saldaturi-molibdenu. L-istandard ASTM A335/A335M ikopri gradi multipli tal-azzar liga ferritika, inklużi P1, P2, P5, P5B, P5C, P9, P11, P12, P21, P22, P23, P36, P91 (Tip 1, Tip 2), P92, eċċ Il-pajpijiet għandhom firxa tad-dijametru ta 'barra ta' 21.3 mm sa 762 mm u a firxa ta 'ħxuna tal-ħajt ta' 2.0 mm sa 130 mm, iddisinjati biex jissodisfaw ir-rekwiżiti dimensjonali għal diversi sistemi ta' pajpijiet ta'-temperatura għolja.
A335 Kompożizzjoni Kimika
| Element | P1 | P2 | P5 | P9 | P11 | P22 | P91 | P92 |
|---|---|---|---|---|---|---|---|---|
| Karbonju (C) | 0.10-0.20 | 0.05-0.15 | 0.15 max | 0.15 max | 0.05-0.15 | 0.05-0.15 | 0.08-0.12 | 0.07-0.13 |
| Manganiż (Mn) | 0.30-0.80 | 0.30-0.61 | 0.30-0.60 | 0.30-0.60 | 0.30-0.60 | 0.30-0.60 | 0.30-0.60 | 0.30-0.60 |
| Fosfru (P) | 0.025 max | 0.025 max | 0.025 max | 0.025 max | 0.025 max | 0.025 max | 0.020 max | 0.020 max |
| Kubrit (S) | 0.025 max | 0.025 max | 0.025 max | 0.025 max | 0.025 max | 0.025 max | 0.010 max | 0.010 max |
| Silikon (Si) | 0.50 max | 0.50 max | 0.50 max | 0.25-1.00 | 0.50-1.00 | 0.50 max | 0.20-0.50 | 0.50 max |
| Kromju (Cr) | 0.50-0.80 | 0.50-0.81 | 4.00-6.00 | 4.00-6.00 | 1.00-1.50 | 1.90-2.60 | 8.00-9.50 | 8.50-9.50 |
| Molibdenu (Mo) | 0.44-0.65 | 0.44-0.65 | 0.45-0.65 | 0.90-1.10 | 0.44-0.65 | 0.85-1.05 | 0.85-1.05 | 0.30-0.60 |
| Vanadju (V) | – | – | – | – | – | – | 0.18-0.25 | 0.15-0.25 |
| Nitroġenu (N) | – | – | – | – | – | – | 0.03-0.07 | 0.03-0.07 |
A335 Proprjetajiet Mekkaniċi
| Proprjetà | P1 | P2 | P5 | P9 | P11 | P22 | P91 | P92 |
|---|---|---|---|---|---|---|---|---|
| Qawwa tat-tensjoni, min (MPa) | 380 (55,000) | 415 (60,000) | 415 (60,000) | 415 (60,000) | 415 (60,000) | 415 (60,000) | 585 (85,000) | 620 (90,000) |
| Qawwa tar-Rendiment, min (MPa) | 205 (30,000) | 205 (30,000) | 205 (30,000) | 205 (30,000) | 205 (30 |
Speċifikazzjoni ta 'A335/SA335 Alloy Pipe
Tip: Pajp ta 'l-azzar mingħajr saldatura, pajp ta' l-azzar mingħajr saldatura ta 'liga
Speċifikazzjoni: OD: 1/2″ – 30″, Skedi: 20, 30, 40, STD, 60, XS, 80, 100, 120, 140, 160, XXS. Tul: 6m, 12m jew personalizzati.
Standard: ASTM A335, ASME SA335
Gradi: GR P5, P9, P11, P12, P22, P91, P92.
Tmiem: Truf Lixxi, Truf Beveled, Truf bil-kamin, Akkoppjar
Wiċċ: Oiled, Iswed miżbugħ biex jipprevjeni s-sadid, illustrat, verniċ, 3PE, FBE
a335 materjal ekwivalenti
| Werkstoff /DIN | MT | ASTM |
|---|---|---|
| 1.5415 | 16Mo3 | A335 Grad P1 |
| 1.7335 | 13CrMo4-5 | A335 Grad P11, P12 |
| 1.738 | 10CrMo9-10 | A335 Grad P22 |
| 1.7362 | X11CrMo5 | A335 Grad P5 |
| A335 Grad P9 | ||
| 1.4903 | X10CrMoVNb9-1 | A335 Grad P91 |
Tabella ta' Paragun ASTM A335 vs ASTM A182
| Parametru | ASTM A335 | ASTM A182 |
|---|---|---|
| Tip ta' Prodott | Pajp mingħajr saldatura | Fittings foloz (Flanges, Valvoli, eċċ.) |
| Manifattura | Hot-Irrumblat/Kesaħ-Proċess Seamless Miġbud | Miftuħ-Die/Magħluq-Die Forging + Makkinar |
| Skop tal-Materjal | Cr-Mo Alloy Steel | Stainless Steel/Cr-Mo Alloy Steel |
| Gradi Tipiċi | P5, P9, P11, P91 | F5, F9, F11, F91, F304, F316 |
| Focus Qawwa | Qawwa Axjali Uniformi | Isotropija Għolja (Raffinament tal-Qamħ Forġa) |
| Spezzjoni Ewlenin | Test Hydro + Ittestjar Ultrasoniku (UT) | Test Penetrant Likwidu + Mikrostruttura |
| Formola tal-Prodott | Straight/U-Liwja Pajpijiet | Flanġijiet, Valvoli, Tees, Minkbejn |
| Temperatura Max | Inqas minn jew ugwali għal 650 grad (P91) | Inqas minn jew ugwali għal 800 grad (F321H Austenitic SS) |
| Reżistenza għall-Pressjoni | Tagħbija ta' Stress Għoli taċ-Ċrieki | Reżistenza Għolja għall-Stress Lokali (eż. Għonuq tal-Fanġ) |
| Applikazzjonijiet | Pajpijiet tal-Proċess Prinċipali (Fwar/O&G) | Komponenti tal-Konfini tal-Pressjoni |
| Kumplimentarjetà | Korp Prinċipali tal-pajpijiet | Tgħaqqad Pajpijiet A335 |
Test u spezzjoni
- Test Tensili
- Test tal-ebusija
- Test idrostatiku
- Ittestjar mhux-distruttiv (NDT)
- Test tal-Impatt