ASTM A335 Grad P91 Alloy Steel Pajpijiet mingħajr saldatura
Oct 13, 2023
ASTM A335 Grad P91 Alloy Steel Pajpijiet mingħajr saldatura
| Speċjalizzati fi | Dijametru Kbir Daqs |
| Dimensjonijiet ta 'barra | 19.05mm - 114.3mm |
| Ħxuna tal-ħajt | 2.0mm - 14 mm |
| Tul | max 16000mm |
| Skeda | Skeda 20 - Skeda XXS (itqal fuq talba) sa 250 mm thk. |
| Formola | Round, Pjazza, Rettangolari, Idrawliku Eċċ. |
| Standard | ASTM A335 P91, SA335 P91 (b'Ċertifikat tat-Test IBR) |
| Daqs | 1/2 NB sa 36 NB |
| Ħxuna | 3-12mm |
| Skeda | SCH 40, SCH 80, SCH 160, SCH XS, SCH XXS, L-iskedi kollha |
| Oriġini | Ewropew, Ġappuniż, Korean, US, Indjan (Strictament Nru Materjal Ċiniż) |
| Tolleranza | Pajp miġbud fil-kesħa: +/-0.1mm Pajp irrumblat kiesaħ: +/-0.05mm |
| Inġenji | Cold rolled u Cold drawn |
| Tip | Seamless / ERW / Iwweldjat / Fabbrikat |
| Tul | Uniku Random, Doppju Random & Tul maqtugħ. |
| Tmiem | Tmiem Plain, Tmiem Beveled, Treaded |
| Speċjalizzati fi | Dijametru Kbir SA335 P91 Materjal |
| Ittestjar Addizzjonali | NACE MR 0175, NACE TM0177, NACE TM0284, TEST HIC, TEST SSC, SERVIZZ H2, IBR, eċċ. |
| Applikazzjoni | Liga ferritika mingħajr saldaturi-Pajp ta' l-Azzar għal servizz ta'-temperatura għolja |
ASTM A335 Grad P91 Proprjetajiet
Proprjetajiet Kimiċi
| Karbonju | Silikon | Manganiż | Fosfru | Kubrit | Molibdenu | Nikil | Kromju | Ram | Oħrajn |
|---|---|---|---|---|---|---|---|---|---|
| 0.08-0.12 | 0.20-0.50 | 0.30-0.60 | 0.02 | 0.01 | 0.85-1.05 | – | 8.00-9.50 | – | – |
Proprjetajiet Mekkaniċi
| Qawwa tar-Rendiment | Qawwa tat-tensjoni | Titwil A5 min | |||
|---|---|---|---|---|---|
| MPa min | ksi min | MPa min | MPa min | ksi min | Persentaġġ |
| 415 | – | 60 | 20 | ||
Denominazzjoni Ekwivalenti
| DIN | MT | BS | NFA | ASTM | ASME |
|---|---|---|---|---|---|
| DIN 17175 Grad X10CrMoVNb9 | – | NFA A 49-219 Grad TU Z 10 CDVN | ASTM A335 Grad P91 | ASME SA 335 Grad P91 | – |